Permanent Magnet Synchronous Machines (PMSM) have gradually become the mainstream solution for drive motors. One main trend for advanced PMSM optimization is focused on new material application. Conventional PMSM iron core is fabricated by Non Grain-Oriented (NGO) silicon steel sheet lamination, based on traditional technic, the high-strength NGO silicon steel uses solid solution strengthening and precipitation strengthening methods to enhance mechanical strength [1].&lt;br/&gt;As mentioned in [2-3], due to the increase in mechanical strength of high-strength NGO steel, a narrower magnetic bridge design can be applied in the rotor design. Thereby reducing the leakage flux to increase the output torque and the overall efficiency. Even though the high-strength NGO had higher iron loss, counting the reduction in the rotor bridge width, the overall performance can be significantly enhanced.&lt;br/&gt;The maximum speed of advanced PMSM is mostly greater than 12000rpm, thus the rotor sustains significant tensile stress due to centrifugal force. It’s easier to form the striped 180° domain with higher permeability under tensile stress [4]. While the frequency influence and thermal condition has not been discussed in [4]. In this paper, we designed an equivalent sample to simulate the condition of an iron core, similarly in [5], with different excitation and manufacture parameter such as laminated number and thermal condition.&lt;br/&gt;Three types of high-strength NGO (SW35YS600\SW35YS900\B35AHS500) and a controlled group (conventional NGO B35A270) has been tested. Magnetic performance of equivalent sample is measured by ring sample method. Two narrow sides of the sample are subjected to large tensile stress concentration, the lamination number is 5, 10, and 20. At high excitation frequencies, the level of iron loss improvement caused by tensile stress is significant.&lt;br/&gt;Four materials have also been annealed respectively at 720°C for 10 hours under argon atmosphere. After annealing, the tensile stress has lower effect on the magnetic properties for B35AHS500 and B35A270, but is significant for SW35YS600 and SW35YS900. Therefore, it is speculated that a large proportion of heat treatment process has been adopted during SW35YS600 and SW35YS900.&lt;br/&gt;In addition, we also conduct metallographic experimental observations on the material of the sample and the tensile fracture, and analyze the reasons for this result at the grain level. And in the subsequent experiment process, we further explored the influence of different environmental temperatures and different tensile stresses on the magnetic properties of these four NGO materials.

**References:**

[1] GONG, Jian, and Hai-wen LUO. &quot;Progress on the research of high-strength non-oriented silicon steel sheets in traction motors of hybrid/electrical vehicles.&quot; Journal of Materials Engineering 43.6 (2015): 102-112.&lt;br/&gt;[2] Tietz, Marco, et al. &quot;Effects and advantages of high-strength non grain oriented (NGO) electrical steel for traction drives.&quot; 2013 3rd International Electric Drives Production Conference (EDPC). IEEE, 2013.&lt;br/&gt;[3] Tanaka, Ichiro, et al. &quot;Application of high-strength nonoriented electrical steel to interior permanent magnet synchronous motor.&quot; IEEE transactions on magnetics 49.6 (2012): 2997-3001.&lt;br/&gt;[4] Senda, Kunihiro, et al. &quot;Magnetic properties and domain structure of non-oriented electrical steel under stress.&quot; IJTFM 131.10 (2011): 884-890.&lt;br/&gt;[5] Gao, Lingyu, et al. &quot;Application of grain-oriented electrical steel used in super-high speed electric machines.&quot; AIP Advances 10.1 (2020): 015127.

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/ccde1a3a9953b57d9bd60bd246980599.jpg)
metallographic experimental observations

![](https://assets.underline.io/uploads/markdown_image/1/image/793eec53db2c5ec9c61420c606acc711.jpg)
sample of the tensile experiment and result of the magnetic test

INTERMAG 2021

 Magnetic Performance Improvement caused by Tensile Stress in Equivalent Iron Core fabricated by High-Strength Non-Oriented Electrical Steel

The 15th Joint MMM-INTERMAG Conference (2022 Joint) is sponsored jointly by AIP Publishing and the IEEE Magnetics Society. Members of the international scientific and engineering communities interested in recent developments in fundamental and applied magnetism are invited to attend and contribute to the technical sessions. The technical program will include invited and contributed papers in oral and poster sessions, invited symposia, a plenary session, and an evening session, with about 1500 presentations overall. This Conference provides an outstanding opportunity for worldwide participants to meet their colleagues and collaborators and discuss developments in all areas of magnetism research.

The 2022 Joint Conference will offer both in-person and prerecorded on-demand content.

For tickets to the event, please register at the following link: https://magnetism.org/register

Please register for the Joint MMM-Intermag conference to join the event.

2022 Joint MMM-INTERMAG

This Conference provides an outstanding opportunity for worldwide participants to meet their colleagues and collaborators and discuss developments in all areas of magnetism research.

Permanent Magnet Synchronous Machines (PMSM) have gradually become the mainstream solution for drive motors. One main trend for advanced PMSM optimization is focused on new material application. Conventional PMSM iron core is fabricated by Non Grain-Oriented (NGO) silicon steel sheet lamination, based on traditional technic, the high-strength NGO silicon steel uses solid solution strengthening and precipitation strengthening methods to enhance mechanical strength [1]. As mentioned in [2-3], due to the increase in mechanical strength of high-strength NGO steel, a narrower magnetic bridge design can be applied in the rotor design. Thereby reducing the leakage flux to increase the output torque and the overall efficiency. Even though the high-strength NGO had higher iron loss, counting the reduction in the rotor bridge width, the overall performance can be significantly enhanced. The maximum speed of advanced PMSM is mostly greater than 12000rpm, thus the rotor sustains significant tensile stress due to centrifugal force. It’s easier to form the striped 180° domain with higher permeability under tensile stress [4]. While the frequency influence and thermal condition has not been discussed in [4]. In this paper, we designed an equivalent sample to simulate the condition of an iron core, similarly in [5], with different excitation and manufacture parameter such as laminated number and thermal condition. Three types of high-strength NGO (SW35YS600\SW35YS900\B35AHS500) and a controlled group (conventional NGO B35A270) has been tested. Magnetic performance of equivalent sample is measured by ring sample method. Two narrow sides of the sample are subjected to large tensile stress concentration, the lamination number is 5, 10, and 20. At high excitation frequencies, the level of iron loss improvement caused by tensile stress is significant. Four materials have also been annealed respectively at 720°C for 10 hours under argon atmosphere. After annealing, the tensile stress has lower effect on the magnetic properties for B35AHS500 and B35A270, but is significant for SW35YS600 and SW35YS900. Therefore, it is speculated that a large proportion of heat treatment process has been adopted during SW35YS600 and SW35YS900. In addition, we also conduct metallographic experimental observations on the material of the sample and the tensile fracture, and analyze the reasons for this result at the grain level. And in the subsequent experiment process, we further explored the influence of different environmental temperatures and different tensile stresses on the magnetic properties of these four NGO materials.

**References:**

[1] GONG, Jian, and Hai-wen LUO. "Progress on the research of high-strength non-oriented silicon steel sheets in traction motors of hybrid/electrical vehicles." Journal of Materials Engineering 43.6 (2015): 102-112. [2] Tietz, Marco, et al. "Effects and advantages of high-strength non grain oriented (NGO) electrical steel for traction drives." 2013 3rd International Electric Drives Production Conference (EDPC). IEEE, 2013. [3] Tanaka, Ichiro, et al. "Application of high-strength nonoriented electrical steel to interior permanent magnet synchronous motor." IEEE transactions on magnetics 49.6 (2012): 2997-3001. [4] Senda, Kunihiro, et al. "Magnetic properties and domain structure of non-oriented electrical steel under stress." IJTFM 131.10 (2011): 884-890. [5] Gao, Lingyu, et al. "Application of grain-oriented electrical steel used in super-high speed electric machines." AIP Advances 10.1 (2020): 015127.

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/ccde1a3a9953b57d9bd60bd246980599.jpg)
metallographic experimental observations

![](https://assets.underline.io/uploads/markdown_image/1/image/793eec53db2c5ec9c61420c606acc711.jpg)
sample of the tensile experiment and result of the magnetic test

poster

INTERMAG 2021 Welcome Video



	
<figure class="video_container">
 <iframe src="https://screencast-o-matic.com/player/crflqFVnUpZ?v=6&ff=1&title=0&controls=1" width=640 height=360 frameborder="0" allowfullscreen="true"> </iframe>
</figure>

Want to buy a ticket? 

Register for INTERMAG 2021 here

[![](https://assets.underline.io/uploads/markdown_image/1/image/17ce76e7960db633258024eef8d6da7f.png)](https://intermag.org/register)

Got your ticket, but still can’t access the event?

Contact us and our team will look into it.

Introduction The metastable α”-Fe16N2 is considered as a candidate for rare earth free semi-hard magnetic materials [1]. It is necessary to improve magnetocrystalline anisotropy of α”-Fe16N2 to obtain higher coercivity Hc [2]. Many theoretical calculations and thin film experiments substituting Fe with some elements such as Co, Ni, Mn, Al, etc. have been done. For example, Co is suggested to increase in magnetocrystalline anisotropy [3]. As one of the synthesis methods of α”-Fe16N2 nanoparticles, it is well known that the nitridation of α-Fe nanoparticles produced by reduction of iron hydroxide such as α-FeOOH. Previously, we have reported that the influence of substituting Co, Al for Fe by synthesizing α”-(Fe, Co)16N2 or α”-(Fe, Al)16N2 nanoparticles [5] and revealed that Co substitution results in the temperature regimes for reduction and nitridation were confirmed to very narrow limits, on the other hand Al substitution brings the wider temperature regimes. In this paper, in order to investigate the complex substitution effect of Fe by Co and Al, we challenged to the synthesis of α”-(Fe0.95Co0.02Al0.03)16N2 nanoparticles by hydrogen reduction of α-(Fe0.95Co0.02Al0.03)OOH as a starting material and subsequent nitridation. Experimental We used commercially available α-(Fe1-xMx)OOH (M= Co, Al, x= 0, 0.02, 0.05) and α-(Fe0.95Co0.02Al0.03)OOH nanoparticles as a starting material. The conditions for reduction and nitridation were systematically examined to obtain higher yield of α”-(Fe1-xMx)16N2 or α”-(Fe0.95Co0.02Al0.03)16N2 according to the following procedure. The α-(Fe1-xMx)OOH nanoparticles were first reduced at 300 - 500 °C for 4 hours in a H2 gas flow. Nitridation was subsequently performed at 150 - 180 °C for 5 hours in an NH3 gas flow. Crystallite diameter Dc of reduced α-Fe1-xMx nanoparticles was measured as average diameter of nanoparticles using Scherrer’s formula based on X-ray diffraction (XRD) with Co Kα radiation. Morphological changes were observed using transmission electron microscopy (TEM). For magnetic properties measurements, these nanoparticles were packed into a disk shape (6 mm diameter, 1 mm thick) with resin. Magnetization M15k and coercivity Hc were measured using vibrating sample magnetometer (VSM) with a maximum applied magnetic field of 15k Oe. Results Fig. 1 (a) shows the regions in the nitridation temperature versus reduction temperature diagrams corresponding to where the α”-phase was produced. M15k and Hc values of the assembled nanoparticles are also indicated. α”-phase was produced under the limited conditions of reduction temperature of 340 °C and nitridation temperature of 170 °C for starting from α-(Fe0.98Co0.02)OOH. On the contrary, α”-phase was produced under broad conditions of reduction temperatures of 400 - 500 °C and nitridation temperatures of 155 - 170 °C for starting from α-(Fe0.98Al0.02)OOH. In the case of starting from α-(Fe0.95Co0.02Al0.03)OOH, α”-phase was produced under the conditions of reduction temperatures of 400 - 500 °C and nitridation temperature of 160 °C. The conditions of α”-phase production were broadened by Al addition to Co. Fig. 1 (b) shows TEM images for the nanoparticles after nitridation starting from α-(Fe0.98Co0.02)OOH, α-(Fe0.95Al0.05)OOH and α-(Fe0.95Co0.02Al0.03)OOH. These nanoparticles are synthesized with hydrogen reduction at 340 °C for 4 hours and subsequent nitridation at 170 °C for 5 hours for α-(Fe0.98Co0.02)OOH, and with hydrogen reduction at 400 °C for 4 hours and subsequent nitridation at 160 °C for 5 hours for α-(Fe0.98Co0.02)OOH and α-(Fe0.95Co0.02Al0.03)OOH, respectively. The particle size of nanoparticles after nitridation starting from α-(Fe0.98Co0.02Al0.03)OOH are between the ones of starting from (Fe0.98Co0.02)OOH and α-(Fe0.95Al0.05)OOH. This result suggested that Al was effective to avoid sintering during reduction. Fig. 2 (a) shows the relationship between M15k and Hc for the nanoparticles after nitridation starting from α-(Fe0.98Co0.02)OOH, α-(Fe0.95Al0.05)OOH and α-(Fe0.95Co0.02Al0.03)OOH. In the case of starting from α-FeOOH was also shown. Higher Hc were obtained by the complex of Co and Al compared to Co or Al alone. Fig. 2 (b) shows Hc change as a function of Dc of those nanoparticles. This result indicates that there is a good relationship between Hc and Dc regardless additive composition. Hc increases with decrease in Dc. In the case of nanoparticles after nitridation starting from α-(Fe0.95Co0.02Al0.03)OOH gives the smallest Dc of 22 nm and highest Hc of 1800 Oe. It is assumed that Al addition to Co is effective to prevent crystalline growth which leads to high Hc of α”-phase. To clarify the reason of increase in Hc, further precise investigation of the distribution of Al and the relationship between anisotropy field of nanoparticles after nitridation will be presented in this conference.

**References:**

[1] R. Skomski et al., Scr. Mater., 112 (2016) 3 [2] M. Tobise et al., J. Magn. Soc. Jpn, 41 (2017) 58 [3] Y. Jiang et al., AIP Adv., 6 (2016) 056007 [4] L. Ke et al., Phys. Rev. B, 88 (2013) 024404 [5] M. Tobise et al., AIP Adv., 9 (2019) 035233

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/af71dcf495e025c51610d79bc24cb5e1.jpg)
Fig. 1. (a) The regions in the nitridation temperature versus reduction temperature diagrams corresponding to where the α”-phase was produced and M15k and Hc values of the nanoparticles are also indicated. (b) TEM images for the nanoparticles after nitridation starting from the material α-(Fe0.98Co0.02)OOH, α-(Fe0.95Al0.05)OOH and α-(Fe0.98Co0.02Al0.03)OOH.

![](https://assets.underline.io/uploads/markdown_image/1/image/b01b30df78a588a568b32b8156ed275d.jpg)
Fig. 2. (a) The relationship between M15k and Hc for the nanoparticles after nitridation starting from the material α-(Fe0.98Co0.02)OOH, α-(Fe0.95Al0.05)OOH and α-(Fe0.98Co0.02Al0.03)OOH. (b) Hc change as a function of crystalline diameter Dc of those nanoparticles.

 Synthesis of α”-(Fe, M)16N2 nanoparticles obtained by hydrogen reduction and subsequent nitridation starting from α-(Fe, M)OOH (M= Co, Al)

— In this paper, a toolbox baptized “PM-Demag” taking into account the permanent magnet (PM) demagnetization phenomenon has been developed. It is based on a nonlinear demagnetization model which considers the thermal state of the PM and reproduces the knee rounded shape of the B(H) curve. Validations against experimental measurements performed on commercial NdFeB PM are presented. Index Terms— Demagnetization, electrical machines, finite element method, permanent magnet. Nowadays, permanent magnets (PM) are widely used in industry, especially in electrical machines. Their use is expected to grow especially in the context of the energy transition of the 21st century. Like soft magnetic materials, they exhibit nonlinear behavior and hysteresis. The part of the curve situated in the second quadrant of the hysteresis cycle, commonly called the demagnetization curve is of interest because it defines the PM properties and operation. It mainly depends on the temperature and on the applied external field. These two parameters strongly influence the magnetic properties of the PM and can cause reversible or irreversible demagnetization [1]. In the special case of a PM electrical machine, an overheating or a short circuit could lead to partial or total demagnetization of the magnets [2]. In this framework, considering the demagnetization phenomena is necessary to precisely predict the change in the PM characteristics and then the machine performances. The knee in the PM demagnetization curve is crucial for a good knowledge of the magnet state. This state depends on the position of the system operating point (intersection between the load line and the demagnetization curve) with respect to the position of the knee. When the operating point is located in the linear zone, above the knee point (reversible part), the PM keeps its initial performances. However, if the operating point is situated below the knee point (irreversible part), the PM must be considered to be partially demagnetized, the remanent flux density decreases and the PM will operate along a minor hysteresis loop which is often approximated by a recoil line [3]. This phenomenon often occurs in electrical machines (especially on the PM surfaces and edges) and could degrade their performances. The degradation degree depends on the temperatures that the machine could reach and on the PM quality. In this work, a toolbox baptized “PM-Demag” based on a non-linear exponential demagnetization model is developed. The model considers the thermal state and it is expressed as a function of the remanent flux density Br, the coercive field Hc, the relative permeability µr as well as an adjustable coefficient K. All these parameters are themselves expressed as functions of the temperature T. The model parameters are identified from the measurements carried out on a dedicated PM hysteresis meter (HyMpulse of Metis®) for different NdFeB magnets. For example, Fig. 1.a shows the measured B(H) and J(H) demagnetization curves for the N35 NdFeB PM and for different temperatures ranging from room temperature (RT) to 140°C. Figure 1.b shows the simulated B(H) demagnetization curves. The developed “PM-Demag” toolbox will be implemented in code_Carmel, which is a home-made finite element method (FEM) software. Application to an electrical machine is envisaged for the extended paper.

**References:**

[1] &lt;!--[endif]--&gt;Furlani, E.P. (2001) Permanent Magnet and Electromechanical Devices: Materials, Analysis, and Applications. Academic Press, Waltham. &lt;!--[if !supportLists]--&gt;[2] &lt;!--[endif]--&gt;P. Zhou, D. Lin, Y. Xiao, N. Lambert and M. A. Rahman, "Temperature-Dependent Demagnetization Model of Permanent Magnets for Finite Element Analysis," in IEEE Transactions on Magnetics, vol. 48, no. 2, pp. 1031-1034, Feb. 2012, doi: 10.1109/TMAG.2011.2172395. [3] S. Hamidizadeh, N. Alatawneh, R. R. Chromik and D. A. Lowther, "Comparison of Different Demagnetization Models of Permanent Magnet in Machines for Electric Vehicle Application," in IEEE Transactions on Magnetics, vol. 52, no. 5, pp. 1-4, May 2016, Art no. 2100304, doi: 10.1109/TMAG.2015.2513067.

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/dcae2862acc82b67848b462f70ff229a.jpg)
Experimental results [B(H) in solid line].

![](https://assets.underline.io/uploads/markdown_image/1/image/b146435ffa1d737ffdbeeac7ad9eb82f.jpg)
Simulated B(H) demagnetization curves.

 Permanent Magnet Non-linear Demagnetization Model for FEM Simulation Environment

The influence of Ce3+ ions substitution for Fe3+ ions in Ni0.42Zn0.58CexFe2-xO4 (x = 0, 0.02, 0.04, 0.06, 0.08, 0.10) compounds on the selected magnetic properties and structure were investigated. The samples were synthesized by means of wet glycine-nitrate technology annealed at the temperature 1200°C for 6 hours. The wide spectrum of characterization methods were used for the study of relevant properties of synthetized materials. X-ray diffraction patterns were recorded by a diffractometer using conventional X-ray tube (CuKα radiation, λ = 1.5418 Å). EDAX were performed by the SEM JEOL 7600-F equipped with both EDX and WDX system. Temperature dependences of magnetic susceptibility was measured using bridge method. The hysteresis loops were recorded using computer controlled digital hysteresisgraph at the same amplitude of applied field Hmax = 1500 A/m, measured at the frequency f = 50 Hz and at room temperature. The determination of real µ' and imaginary µ'' parts of complex (relative) permeability have been performed by means of an impedance analysis procedure using a vector network analyser Keysight E5063A in the frequency range from 1 MHz to 3 GHz. Results and Discussion XRD results indicate a presence of multi-phase structure. The major is found to be spinel phase and secondary, increasing with the addition of Ce3+ ions, corresponds to CeO2. The final number of possible substitution of Ce3+ ions for Fe3+ ions in the B sites, and the difference in their ionic radii, is the cause of the formation of aggregates on the grain boundary as secondary phase [1]. The distribution of elements and their amounts in weight percentages for NiZnCe samples were studied by means of EDAX analysis. The real content of Ni2+, Zn2+, Ce3+, Fe3+ and O2- shown in Tab. I confirmed the substitution of Fe3+ ions by Ce3+ ions, since the increase of Ce3+ content decreases the amount of Fe3+. Temperature dependences of magnetic susceptibility were recorded within the range from room temperature up to 450°C at rise of 4°C/min. Ferrite powder specimens of amount approximately 50 mg were measured; susceptibility values were related to the same weight (1 mg) for all cases. These dependences are decreasing monotonously and they exhibit one strong drop to paramagnetic state. From that, we can conclude that no unwilled phase is present in the ferrite to a significant extent. Curie temperature TC was determined from the point of inflexion at strong decrease of temperature dependence. Even the paramagnetic substituent (Ce3+) ions occupy B-sites dominantly at expense of Fe3+ ions, it does not change the A-B exchange interactions, because TC remains almost constant [2]. The hysteresis loops exhibit quite complicated behavior. By adding larger amount of Ce3+ ions, the maximum flux density Bmax at given maximum applied field sometimes raises and sometimes decreases comparing to the non-substituted ferrite. Note that the value of Bmax at given maximum applied field Hmax = 1500 A/m approaches the largest value for x = 0.08 (only slightly larger than for x = 0.04). The differences can be explained by the fact that the saturation magnetization is an intrinsic parameter (thus, structurally independent) meanwhile the Bmax corresponds to structurally sensitive behavior of material when magnetizing and approaching the saturation. In addition, coercive field is nearly linearly increasing with increment of x. This behavior is similar to that observed in case of Cu-substituted ferrites with the similar chemical formula (except for Cu instead of Ce), [3]. This may be justified by the complexity of the spinel structure, presence of other crystalline phases, etc. In Fig. 1 the frequency dependences of real µ' and imaginary µ'' parts of complex (relative) permeability µ = µ' - jµ'' are presented for prepared spinel ferrites. The obtained frequency dispersion of complex permeability is caused by the domain wall and ferrimagnetic (or spin precession) resonance [4], [5]. The achieved results may be explained as follows. Magnetic properties of nickel-zinc ferrites as representatives of spinel-like ferrites are affected not only by the method of preparation and chemical structure (and composition), but also by properties such as porosity, crystallite size (or grain size), lattice impurities (or defects), concentration of cations, etc. Also the super exchange interactions may strongly change the resultant properties: in spinel ferrite system AA and BB interactions are poorer than AB interaction. In the prepared ferrites, the shrinkage of lattice is present because of the larger ionic radius of cations such as Ce3+ (1.143Å), Zn2+ (0.74Å) and Ni2+ (0.69Å) in comparison with Fe3+ (0.65Å). The magnetic moments of these cations are as follows (in Bohr magnetons): 2.5µB, 0µB, 2.3µB and 5µB. Values of magnetic moments relates the cation distribution of Ni0.42Zn0.58CexFe2-xO4 ferrite system (Ce3+ ions have preference on B sites): (Zn0.582+Fe1-x3+)A[Ni0.422+Cex3+Fe1+x3+]BO42-. Due to the values of ionic radius and magnetic moment, Ce3+ ions replace more Fe3+ ions in the crystal lattice and this leads to the raise of coercive field which in turns changes the value of permeability [5], [6]. Conclusion From the above experimental results, it can be seen that adding even a small amount of cerium element has evident influence on selected properties. Consequently, by adding defined amount of Ce3+ ions, the desired parameters can be easily controlled by a straightforward way and thus tailored for any particular application required in industrial practice.

**References:**

[1] R. S. Yadav, J. Havlica, J. Masilko, J. Magn. Magn. Mater., Vol. 399, pp. 109-117 (2016) [2] M. A. Ahmed, S. F. Mansour, S. I. El-Dek, Solid State Ionics, Vol. 181, pp. 1149-1155 (2010) [3] J. Sláma, A. Grusková, M. Ušáková, J. Magn. Magn. Mater., Vol. 321, pp. 3346-3351 (2009) [4] M. Šoka, R. Dosoudil, M. Ušáková, Acta Phys. Pol. A, Vol. 131, pp. 690-692 (2017) [5] R. Dosoudil, M. Ušáková, A. Grusková, IEEE Trans. Magn., Vol. 50, no. 4 (2014) [6] M. N. Akhtar, M. A. Khan, J. Magn. Magn. Mater., Vol. 460, pp. 268-277 (2018)

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/eccf1c3546b0486f5775ad28c48f37bb.jpg)

![](https://assets.underline.io/uploads/markdown_image/1/image/2358bea70a2a67441e24abb7319de58f.jpg)

 Magnetic and Structural Properties Analysis of Cerium Substituted Nickel Zinc Ferrites

Rare heart substituted iron garnets (REIG) are characterized by a high magnetic susceptibility that results in a large magnetization in the presence of small magnetic fields [1]. The magnetic microstructures are influenced by natural or artificial defects; in particular, domain walls (DWs) undergo to nucleation, segmentation and pinning in correspondence to them. In REIG with in-plane spontaneous magnetization, the Néel spike domain structure is one of the most common magnetic microstructure nucleated at microdefects and its charged DWs can produce not negligible stray fields above the REIG. These DWs are interesting both for fundamental studies and for innovative applications such as micro positioning by contactless actuators [2]. To make the most out of this, performing a quantitative analysis is crucial. The experimental characterization by means of quantitative magneto-optical imaging with an indicator film [3] showed that stray fields are detectable above the surface of (Lu, Bi) substituted iron garnets, characterized by a spontaneous in-plane magnetization around 150 kA/m, in correspondence of DWs delimiting a Néel spike that is generated by a micro-crack [4]. In order to understand how the externally detected stray fields are correlated to the pattern of the internal magnetization, here we propose 2D and 3D models based on FEM developed through the COMSOL Multiphysics© software. These models take into account the magnetic microstructure of the Néel spike, i.e., either single DWs that run parallel into the bulk of the domain and a couple of DWs at the Néel spike tip (2D) or DWs that merge in a single point (3D). This approach allows us to describe the magnetic microstructure by means of CAD defined patterns, whose complex structure can be implemented easily in the FEM simulation. It turns out that the results are in agreement both with experiments and with previous numerical calculations performed with a simplified model in MATLAB© [4]. The comparison with experiments allowed us also to determine the distance of measurement between the indicator film of MOI experiments and the REIG under investigation. Figure 1 shows linear profiles across the DWs, along with experimental data. The distance of measurement is about 7 μm and the magnetic induction at the tip of the Néel spike is twice the value found for the single charged DW at the domain boundary. The simplicity of the 2D model limits the computational cost required; on the other hand, the 3D simulation can be useful for reproducing in detail the stray field distribution generated by the complex structure of the Néel spike domain, as shown in Figure 2. In summary, we validated these models for reproducing the stray field distribution above charged DWs, opening the way for the design of artificial structures in order to obtain controlled magnetic patterns, thanks to the powerful 3D engine of the COMSOL Multiphysics© software.

**References:**

[1] L. E. Helseth, M. Kurniawan, R. W. Hansen, and T. H. Johansen, PHYSICAL REVIEW B77, 064433 (2008) [2] L. E. Helseth, R. W. Hansen, T. H. Johansen, and T. M. Fischer, Appl. Phys. Lett.85, 2556 (2004) [3] F. Laviano, D. Botta, A. Chiodoni, R. Gerbaldo, G. Ghigo, L. Gozzelino, S. Zannella and E. Mezzetti, 16, (2003) 71; Physica B 403 (2008) 293 [4] A. Napolitano, C. Ragusa, S. Guastella, S. Musumeci, P. Rivolo, F. Laviano, JMMM, Vol 504, 2020, 166556 [5] O. Khan, C. Ragusa, and F. Khan, IEEE transactions on magnetics, vol. 50, no. 11, November 2014

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/7f0da98d3c563c66b54b53692a817a42.jpg)
Figure 1. Cross sectional profiles of the stray field, simulated and experimental values, for a single DW (a) and the tip of the Nèel spike (b).

![](https://assets.underline.io/uploads/markdown_image/1/image/2928dd60fc86135c15716d29f81cc2da.jpg)
Figure 2. Magnetic field distribution of the stray field above a Néel spike: 3D plot of the magnetic induction intensity that clearly shows the stray field peak in correspondence to the tip of the Nèel spike. The distance of measurement was chosen on the basis of the previous comparison between experimental data and 2D simulations.

 Modeling stray-field distribution generated by domain-walls in rare-earth substituted iron garnets

Intensive research on soft magnetic nanoparticles has been attracted by biomedical applications such as MRI markers and cancer therapy by magnetic hyperthermia. These nanoparticles can also be used in additive manufacturing processes, such as inkjet printing, to elaborate magnetic coatings to meet emerging needs such as RFID antenna shielding or wireless power transfer. The nanoparticles are synthesized by thermal decomposition with organic solvents. Two different ways of heating are employed: the conventional one using a heating mantle and the other one using a microwave oven[1]. A good control of the particle size of Fe3O4 through the addition of ethylene glycol has been reported2. Other groups have used this technique to synthesize core-shell Fe3O4 nanoparticles. We have synthetized nanoparticles of mixed oxides ZnxFe3-xO4, where the magnetic and dielectric properties can be tuned by the Zn/Fe ratio[2]. The two processing methods were compared in order to determine the most appropriate way to control the size and morphology spread of the obtained nanoparticles. The influence of the microstructure on the magnetic properties of Zn0.4Fe2.6O4 and Zn0.2Fe2.8O4 (theoretical compositions) nanoparticles was studied by X-ray diffraction analysis and 57Fe Mössbauer spectrometry, under zero field and in-field. Experimental details: The conventional way in a heating mantle allows obtaining various morphologies: cubes, octahedra... However, it induces heterogeneity in terms of size and shape in a batch, due to insufficient monitoring of the temperature during the reaction. The microwave-assisted thermal decomposition enables a fast and more uniform heating, leading reproducibly to nanoparticles with homogeneous size and shape. The difference lies in the choice of solvents and surfactants: respectively benzyl ether and oleic acid for the conventional thermal decomposition, and octadecene for the solvent with a combination of oleic acid and oleylamine for the surfactant for the microwave reactor. These surfactants have two complementary functions in the synthesis. Oleic acid stimulates the growth of nanoparticles along a preferential axis while oleylamine, in addition to redox possibilities, slows down the nanoparticle growth[3]. Tuning their compositional ratio yields a good control of the nanoparticle morphology. Results: The morphology and the size were observed by scanning electron microscopy and transmission electron microscopy. Two different morphologies are highlighted. While 5 nm-nanoparticles (written SP(F)M) are quite spherical, the 35 nm-particles (FM) have a “raspberry” morphology (Fig. 1). These observations are consistent with those of Y-J. Liang’s1 on 50 nm particles. It should be assimilated to a binding between crystallites and the continuity of the crystal planes in a raspberry structure is noticed, as observed by S. Begin-Colin’s group[4] with structures of about 250 nm. The phase purity was probed by X-ray diffraction (XRD). The size of the coherent diffraction domains was calculated with two different methods: using Scherrer’s formula, and through a Rietveld refinement. The results are compared and correlated to TEM observations. The saturation magnetization was determined through the hysteresis cycles measured with a vibrating sample magnetometer (VSM) at room temperature. The superparamagnetism is observed for the 5 nm particles. The magnetization curve has been fitted with a Langevin function[5] which allows recovering the intrinsic saturation magnetization and an apparent size of 5 nm, close to that observed by TEM. The intrinsic saturation magnetization (85.6 emu/g) from the model is in good agreement with that determined at 2 K with a VSM/SQUID (85 emu/g). The saturation magnetization of the two types of nanoparticles is lower (85.6 emu/g for the 5 nm and 80.6 emu/g for the 35 nm) than that of the bulk ferrite Zn0.4Fe2.6O4 which is about 98.8 emu/g. Several contributions have to be taken into account to explain this discrepancy: - A surface spin-canting effect[6] could impact the magnetic moment of particles, especially for the smallest ones. The thickness of the surface spin-canting was estimated and the magnetic moments were thus corrected (Fig. 2). - A cationic disorder with a fraction of Zn2+ ions at the octahedral sites of the spinel structure, and not only at the tetrahedral (A) ones, can be deduced from a Rietveld analysis of X-ray patterns, and in-field Mössbauer spectra. Indeed, these techniques have made it possible to quantify the distribution of cations at the tetrahedral (A) and octahedral (B) sites of the spinel, and thus to calculate the magnetization according to a molecular field model[7] (Fig. 2). - Oxidation of the nanoparticles with conversion of Fe2+ into Fe3+ could lead to the reduction of the saturation magnetization[8]. The analysis of Mössbauer spectra enables to recover values close to the measured magnetic moments, which makes the cations distribution reliable. It therefore makes it possible to predict a magnetic moment close to the experimental one, keeping a spinel-type chemical formula with presence of vacancies to take into account the oxidation of the theoretical composition. The understanding of the effect of the microstructure on the magnetic moment opens up possibilities by tuning magnetic properties of iron oxide nanoparticles.

**References:**

[1] Y-J. Liang, F. Fan and M. Ma, Colloids and Surfaces A., Vol. 530, p.191-199 (2017) [2] A. Fujiwara, M. Tada and T. Nakagawa, J. Magn. Magn. Mater., Vol. 320, p.L67-L69 (2008) [3] S. Mourdikoudis and L. M. Liz-Marzán, Chem. Mater., Vol. 25, no. 9, p.1465–1476 (2013) [4] O. Gerber, B. Pichon, and C. Ulhaq, J. Phys. Chem. C., Vol. 119, p.24665-24673 (2015) [5] J.L. Dormann, D. Fiorani and E. Tronc, Adv. Chem. Phys., Vol. 98, p.283-494 (1997) [6] E. Tronc, P. Prené, J.P. Jolivet, J.L. Dormann and J-M. Greneche, Hyper. Inter., Vol. 112, p.97-100 (1997) [7] P. G. Bercoff and H. R. Bertorello, J. Magn. Magn. Mater., Vol. 169, p.314–322 (1997) [8] A. Demortiere, P. Panissod and B.P. Pichon, Nanoscale., Vol. 3, p.225-232 (2011)

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/d0fab6a72fe682a60b495b03c6b78453.jpg)
Fig. 1. TEM picture of raspberry-like nanoparticles

![](https://assets.underline.io/uploads/markdown_image/1/image/3f6da719018112feef39b97921fb4966.jpg)
Fig. 2. Magnetic moments predicted from microstructural characterizations for SP(F)M and FM particles with different Zn contents (0.2 and 0.4).

 Quantitative retrieving of the magnetic moment of iron oxide nanoparticles through structural characterizations

A new intermetallic ternary compound La6Pd2.28Sb15 was synthesized from the reaction of lanthanum and palladium metals in a molten antimony flux. The compound crystallizes in the orthorhombic space group Immm with a= 4.3082(9) Å, b=15.399(3) Å, and c=19.689(4) Å. The crystal structure contains a three-dimensional framework of Sb squares and ribbons that extend along the a axis, including complex Sb–Sb bonding. Magnetization measurements indicate that the intrinsic magnetic behavior of La6Pd2+xSb15 (x = 0.28) is diamagnetic, which we associate with Landau diamagnetism slightly larger than Pauli paramagnetism in this compound. The resistivity (ρ) decreases when lowering the temperature, indicating metallic behavior, and at low temperatures r depends quadratically on T. Interestingly, both the Hall resistivity and magnetoresistance present a nonlinear dependence on the applied magnetic field, suggesting a multiband behavior. This is supported by density-functional electronic structure calculations which show a complex Fermi surface originated in the antimonide substructures and containing both electron and hole pockets as well as open sheets.

**References:**

M. I. Sturza, M. L. Amigó, J. I. Facio et al., Journal of Solid State Chemistry, Vol. 291, pp. 121578 (2020),

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/809fee0358e093416661fd556c5c2f76.jpg)
Fig 1. Ball-and-stick representations of three-dimensional structure of La6Pd2+xSb15 (x = 0.28) viewed down the crystallographic a-axis. The red dashed lines outline the La6 trigonal prisms.

![](https://assets.underline.io/uploads/markdown_image/1/image/0a2b239811e304dece46ec3eebd0d4db.jpg)
Fig 2. Temperature dependence of the susceptibility for zero field cooling (ZFC) and field cooling (FC) procedures. Inset: Field dependence of the magnetization for several temperatures. In all cases, the background of the glue and the sample holder was subtracted, as well as, the core diamagnetic contribution.

 La6Pd2+xSb15 (x = 0.28): A Rare-earth Palladium Intermetallic Compound with Extended Pnictogen Ribbons

Heusler alloys have been intensively investigated to develop functional materials as half-metals, shape memory alloys, and thermoelectric conversion materials. Heusler alloy Co2TiZ (Z = Si, Ge, Sn) was expected to be a half-metal with characteristics of Weyl fermions by first-principles band calculations [1]. The Weyl semimetals are of great interest materials, due to their unusual magnetoelectronic and magnetothermal properties. In the case of magnetic materials, the spatial and temporal correlations of the magnetization M(r,t) show a tendency to diverge at the critical temperature. The phenomenon in which magnetic properties show peculiar temperature and magnetic field dependence at the critical temperature is called a critical phenomenon. The critical exponent δ is defined at T = TC by H = DM(T,H)δ . (1) In later work, to find the critical exponent δ, the temperature at which the plot, taking logarithms on both sides of equation (1), is linear in log(M)-log(H) scale is defined as the Curie temperature TC [2]. Theoretically, the molecular field theory predicts δ = 3.0, the three-dimensional Heisenberg model δ = 4.80 [2], the three-dimensional Ising model δ = 4.82 [2], and the spin fluctuation theory by Takahashi δ = 5.0 [3]. For half-metals with characteristics of Weyl fermions, there are few reports of systematic analyses of the critical exponents. Therefore, we focus on the element substitution effect between Co2TiSn and Co2TiGa. Co2TiSn possesses characteristics of both half-metal and Weyl fermions, and Co2TiGa is the itinerant electron ferromagnet with the high spin polarization. We measured the magnetization in the mixed crystal compound Co2TiGa0.8Sn0.2 and investigated the critical exponent δ near TC. Polycrystalline Co2TiGa0.8Sn0.2 samples were synthesized by arc-melting high-purity constituent elements under high purity Ar atmosphere. To homogenize the synthesized sample, it was annealed at 1100°C for 3 days and then quenched in water. The magnetization of Co2TiGa0.8Sn0.2 was measured using a superconducting quantum interference device (SQUID) (Quantum Design MPMS-XL). From the magnetization measurements of Co2TiGa0.8Sn0.2, the spontaneous magnetization Ms was estimated to be Ms = 0.907 μB/f.u. The critical exponent δ was analyzed from the magnetic field dependence of the magnetization near TC using equation (1). The magnetization curves obtained at each temperature were plotted for log(M/Mmax) against log(H/Hmax) in Fig.1. The values of δ and its fitting error, obtained from the analysis of the magnetization curves in Fig.1, are shown in Fig.2. Since the temperature at which the fitting error is minimized agrees best with equation (1), that temperature can be considered as the Curie temperature TC. From Fig.2, TC = 105 K and δ = 4.45 were obtained. The δ value obtained in this study was different from the value 3 by the molecular field theory, but was close to the value 5 predicted by the spin fluctuation theory for a weakly ferromagnetic itinerant electron system. Therefore, we also reanalyzed the magnetization below 10 kOe, where the magnitude of the applied magnetic field is 1/5 of 50 kOe, because the strong magnetic field may suppress the spin fluctuations. From the analysis of the data below 10 kOe, TC = 104 K and δ = 4.82 were obtained. Thus, a change of δ due to the suppression of the critical fluctuation by the strong applied magnetic field seems to be likely at least in this case. The discrepancy between our results and the theoretical models seem to arise from a distribution of the Curie temperatures in the samples since the δ value changes even at 1 K.

**References:**

[1] G. Chang et al., Sci. Rep. 6, 38839 (2016). [2] M. Seeger et al., Phys. Rev. B 51, 12585 (1995) and References: cited therein. [3] K. Shimizu et al., J. Phys. Soc. Jpn. 59, 305 (1990).

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/bc2f95d7cb6fc566aa6579d1bb42e012.jpg)
Fig.1. The log(M/Mmax)-log(H/Hmax) plots of Co2TiGa0.8Sn0.2 near TC.

![](https://assets.underline.io/uploads/markdown_image/1/image/829df8173ea5fbd2b9218fdb9ac04f21.jpg)
Fig.2. The critical exponent δ and its fitting error of Co2TiGa0.8Sn0.2.

 Critical behavior of the magnetization in Heusler alloy Co2TiGa0.8Sn0.2

Mn2YZ based inverse Heusler alloys with cubic or tetragonal structures and high Curie temperature (TC) display exceptional tunability of their properties either by controlling the degree and the type of atomic ordering [1] or by controlling the total valence electron concentration (VEC) of the alloy [2]. Here the Mn atoms occupy both the (0,0,0) or (½, ½, ½) and (¼, ¼, ¼) or (¾, ¾, ¾) sites in the Heusler structure with antiparallel spins of different magnitude resulting in a ferrimagnetic order. Several theoretical and experimental studies on Mn2YZ alloys have predicted interesting properties like half-metallicity, spin gapless semiconductor with a high magnetic ordering temperature, anomalous hall effect and even zero field exchange bias, spin valve behaviour [3,4] etc. Mn2NiSn is one such cubic ferrimagnetic Heusler alloy with a moderately high magnetic moment of ~2.5 mB [5]. Density functional calculations as well as neutron diffraction studies have shown that the magnetic moment of Mn2NiSn can be tuned by controlling antisite disorder [5,6]. There are also reports suggesting a strong relation between the magnetic moment and the VEC controlled essentially by the Z element in Mn2NiZ alloys [7]. In the present work we aim to understand the role of antisite disorder on the magnetic properties of Mn2NiSn. We have employed two routes to introduce the antisite disorder. Firstly, we have systematically replaced Ni by Mn at the X site in Ni2MnSn by preparing alloys of the type Ni2-xMn1+xSn (where x = 0, 0.25, 0.5, 0.75 and 1) Secondly, the two alloy compositions, Ni1.25Mn1.75Sn (x = 0.75) and Mn2NiSn (x = 1) were subjected to an additional thermal treatment. The alloys were prepared by arc melting constituent elements in argon atmosphere and subsequently annealed at 800 oC for 72 hours in evacuated quartz tubes and quenched in ice cold water (referred to as rapid quenched (RQ)). The arc melted Ni1.25Mn1.75Sn and Mn2NiSn were cut into two halves and were sealed in four different quartz tubes. While two of these tubes containing the respective alloys were quenched from 800oC in ice water, the temperature of the other two tubes with the same compositions as that of the RQ alloys was lowered from 800oC to 427oC after 72 hours of annealing and were annealed at this lower temperature for the next 28 hours and cooled in furnace (referred as FC). All the alloys were characterized by x-ray diffraction (XRD) and SEM-EDX for the determination of their structure and composition. SEM-EDX indicated the compositions to be within 1% of their starting values. Rietveld refinement of the XRD patterns for the RQ alloys showed them to be largely single phase with a cubic L21 Heusler structure (SG: Fm-3m). Small percentage (~ 1 – 2 %) of the MnO impurity phase was noticed in a few compositions. In the case of FC alloys, while Ni1.25Mn1.75Sn alloy was cubic, Mn2NiSn was biphasic with major L21 phase (~93%) and minor (~7%) Mn3Sn type hexagonal phase (SG: P63/mmc) (Fig 1) . Magnetization measurements as a function of temperature (3 K to 390 K) were carried out in 100 Oe applied magnetic field employing zero-field cooling and field cooling protocols. TC increased from 340 K in x = 0 to above the highest measured temperature for all alloys with x =0.5 and above . Isothermal magnetization at 5 K was measured in the field interval of ± 7 T to determine the saturation magnetic moment. All the compositions showed ferromagnetic like M(H) loop with very low coercivity. The saturation magnetization in Ni2MnSn gave an effective moment of 4.06 mB/f.u. good agreement with reported values [8]. In the RQ alloys, with increase in Mn content, the magnetic moment decreases steadily from 4.06 mB/f.u. to 1.93 mB/f.u. in Ni1.25Mn1.75Sn and then increased to 2.80 mB/f.u. in NiMn2Sn. The FC Ni1.25 Mn1.75Sn showed a significant increase in its magnetic moment to 3.31 mB/f.u. This increase is surprising considering its structure to be the same as that of its RQ counterpart. In the phase separated Mn2NiSn the magnetic moment showed a marginal increase to 2.83 mB/f.u. To understand the above magnetic properties, local structures of Ni, Mn and Sn in all the alloys were studies by employing extended x-ray absorption fine structure (EXAFS) spectroscopy. In all the alloys EXAFS data were analysed together using a model based on their respective crystal structure. Excellent fits were obtained for RQ alloys with x = 0, 0.25 and 0.5. In case of Ni1.25Mn1.75Sn, only Ni EXAFS could be well described with the crystal structure model. Both Mn and Sn EXAFS could not be fitted and relaxation of structural constraints indicated a much lower value for the Mn – Sn bond distance than the predicted 3.025 Å from its crystal structure. Introduction of additional Mn – Sn and Mn – Mn correlations derived from hexagonal Mn3Sn resulted in a good fit to the EXAFS data of x = 0.75 and 1 RQ and FC alloys. Mn3Sn like environment can exist in Mn2NiSn type alloys if, in addition to the A2 type disorder, there is also an antisite disorder between Mn and Sn atoms (Fig 2). EXAFS analysis indicated a defect concentration ~ 20 ± 7 % in RQ and FC Mn2NiSn and much less in Ni1.25Mn1.75Sn. Such a segregation of defect within the overall Heusler structure due to antisite disorder seems to be the reason for the increased magnetic moment in Mn2YZ alloys.

**References:**

[1] T. Graf, C. Felser, S. Parkin, Prog. Solid State Chem. 39, 1 (2011). [2] C. Felser, L. Wollmann, S. Chadov, Chem Int Ed. 46:668-99, (2007). [3] S. Ouardi, G. Fecher, C. Felser, Phys. Rev. Lett. 110, 100401 (2013). [4] A. K. Nayak, M. Nicklas, S. Chadov et al, Phys. Rev. Lett. 110, 127204 (2013). [5] R. B. Helmholdt and K. H. J. Buschow, J. Less-Common Met. 128, 167 (1987). [6] S. Paul, A. Kundu, B. Sanyal, J. Appl. Phys. 116, 133903 (2014). [7] H. Luo, G. Liu, F. Meng, J. of Magn. Magn. Mater. 321, 4063–4066 (2009). [8] M. Nazmunnahar, T. Ryba, J. J. delVal, J. of Magn. Magn. Mater. 386, 98–101 (2015).

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/caad83c069f8c7210cc235e36301d783.jpg)
X-ray diffraction patterns for Ni2-xMn1+xSn series of RQ alloys where (x = 0, 0.25, 0.5, 0.75, 1) and Ni1.25Mn1.75Sn, NiMn2Sn FC alloys.

![](https://assets.underline.io/uploads/markdown_image/1/image/147e5a0f09a0160a24d74cfbbc2a0169.jpg)
Schematic diagram of the ab plane of Mn2NiSn showing the segregation of Mn3Sn- type Hexagonal defect phase.

 Antisite disorder and defect phase segregation and its role in magnetic properties of Mn2NiSn

The search for new functional magnetic materials has led to the exploration into multi-component alloys (MCAs), which contain four or more elements with percentages between 12.5 % and 33 %. These include the sub-class of high entropy alloys (HEAs) which often exhibit single phases, thought to be stabilised by the high entropy of mixing of these compounds amongst other competing thermodynamic contributions. The resulting alloys often have interesting functional properties, which are linked to their structure. This work has explored a number of different compositions (CoFeNi0.5Cr0.5Alx, CoFeNi0.5CrxAl CoFeNiCryCux) in both bulk form, to understand how the phases present in the alloys influence the magnetic properties. The work has also used semi-empirical models to predict the different phases within the compositions and machine learning has been used to predict the saturation magnetisation. For example, in bulk CoFeNi0.5Cr0.5Al it was found that Fe-Cr nanoparticles formed in a weakly magnetic CoNiAl matrix [1]. This formation of round nanoparticles increased the magnetisation of the CoFeNi0.5Cr0.5Al alloy by a factor 4 at room temperature. For all the CoFeNi0.5Cr0.5Alx samples, the coercive field was small and the saturation magnetisation comparable with NiFe. While for the bulk CoFeNi0.5CrxAl samples, nanoparticles formed in all the samples containing Cr, with the CoFeNi0.5Cr1.0Al sample having square nanoparticles. Thus the amount of Cr in CoFeNi0.5Al dominates the geometry of the FeCr nanoparticles that form. Plus encapsulating the Cr in Fe-Cr nanoparticles meant that the Curie Temperatures for all the alloys containing Cr and Al were above 300 K (Fig. 1a). While for bulk CoFeNiCryCux (x = 0.0 - 1.5 and y = 0.0 - 1.0) samples, it was found that the addition of Cu could be used to tune the Curie Temperature over a 100 K range, with less than a 30 % reduction in the saturation magnetisation at 10 K, while the addition of Cr changed the Curie Temperature by 700 K and reduced the saturation magnetisation by 60 % at 10 K. By tuning the Cu to Cr ratio it is possible to achieve a Curie temperature around room temperature. The magnetocaloric effect (MCE) was studied in these materials, as the compositions tend to involve cheaper, more widely available elements, plus careful tuning of the composition will allow for the Curie Temperature to be around 300 K. It was found that the refrigeration capacity for the CoFeNiCryCux alloys was ~ 70 J/kg and for the CoFeNi0.5Cr0.5Alx alloys was ~ 75 J/kg at 2 T (Fig. 1b) [2]. Although these are smaller than existing materials such as LaFeSi, these HEAs still have advantages due to the presence of second order transitions, and having a wider operational temperature range for the MCE. In conclusion, the MCAs studied have promising functional magnetic properties, with small coercive fields, and reasonable saturation magnetisations. The phases present can be tuned via the composition, allowing for two-magnetic phase systems to be fabricated, that improve the magnetic properties compared to a single solid solution. The research carried out is only the tip of the iceberg, but these alloys are showing encouraging results.

**References:**

[1] N. A. Morley, C. R. B. Lim, J. Xi, A. Quintana-Nedelcos, and Z. Leong, Scientific Reports, 10, 14506, (2020) [2] A. Quintana-Nedelcos, Z. Leong, and N.A. Morley, Materials Today Energy, (accepted 2021)

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/279780d9001aefe47b6797a2a7923640.jpg)
Figure 1a. Curie Temperature for CoFeNi0.5Cr0.5Alx, CoFeNi0.5CrxAl and CoFeNiCryCux alloys. 1b. Refrigeration capacity at 2 T for CoFeNi0.5Cr0.5Alx, CoFeNi0.5CrxAl and CoFeNiCryCux alloys. Shaded area useful temperature range.

 High Entropy Alloys: The next big thing in functional magnetic alloys

Fe-Co alloys have been ideal materials for various applications where high saturation magnetization (Ms), high permeability (µ) and low coercivity (Hc) are needed, especially for the applications where the minimization of mass and volume is a design parameter, such as aerospace industries [1-6]. In addition, their high Curie temperature makes them competitive candidates for high temperature applications [4]. In this study, in order to fully understand the compositional effect of Fe-Co alloys on their magnetic behaviour, Fe25Co75, Fe50Co50 and Fe75Co25 alloys were produced by using arc melting technique and characterized with the help of X-ray diffraction (XRD) analysis and superconducting quantum interference magnetometer (SQUID). XRD analysis indicated that all the samples were single phase (BCC), proving that oxidation did not occur during the manufacturing process. Furthermore, from their hysteresis loops, their magnetic saturations, remnant magnetizations and coercivities were found in the ranges 253-280 emu/gr, 2.06-6.15 emu/gr and 8.67-40.24 Oe, [4] respectively (Fig. 1). It was observed that as the % Co (wt.) content increases, saturation and remnant magnetization decreases, thus the Fe-rich alloys have higher magnetic properties. Also, after arc melting, stress-relief annealing was employed at 1073 K for 1 hr, resulting in reduction of the magnetic saturation (220-272 emu/gr), remnant magnetization (1.08-3.8 emu/gr) and coercivity (4.73-13.28 Oe) [5] due to the microstructural refinement, as it can be seen clearly in Fig.1. This study confirms that arc melting helps to improve the magnetic properties of Fe-Co alloys, because their magnetic properties is higher than the magnetic properties of those fabricated by mechanical alloying (Ms: 150-225 emu/gr, Hc: 25-70 Oe) [4] and cold rolling (Ms: 217.8 emu/gr, Hc: 87.7 Oe) [3]. Curie temperatures of the as-cast samples (1097-1181 K), are slightly lower than the values in the literature [5], also decreased slightly to the value range of 1071-1107 K after the heat treatment. By looking at Fig. 2, for the high temperature magnetic performances of as cast and annealed specimens, it can be seen that the annealed samples have a higher saturation magnetisation as a function of temperature. Further study has been undertaken to design and develop a new Fe-based amorphous alloy, with similar properties to Fe-Co alloys. The alloy of Fe45Co15B28Al10B2 was arc-melted followed by stress-relief annealing at 573 K for 1 hr to achieve the desired magnetic properties and amorphous morphology. Using DCS and temperature dependence magnetisation measurements up to 1000 K, the temperature dependence structural and magnetic behaviour was studied. DSC analysis indicates that the sample has glassy phase with the melting point of 1200 K and glass transition temperature of 800 K. Moreover, its Curie temperature was found as 940 K. Thus, this composition has promising results as a new soft magnetic material for high temperature applications.

**References:**

[1] S. Bergheul, A. Haddad, H. Tafat and M. Azzaz, “Magnetic , Microwave and Absorbing Properties Fe-Co of Alloy Synthesized by Mechnanical Alloying Process,” in Application of Contemporary Non-Destructive Testing in Engineering, Portoroz, Slovenia, 2005. [2] R. Fingers and G. Kozlowski, “Microstructure and magnetic properties of Fe–Co alloys,” Journal of Applied Physics, vol. 81, no. 8, pp. 4110-4111, 1997. [3] S. Honjo, S. Kikuchi, A. Sakuma, S. Ishio and J. Balachandran, “Preparation of magnetic Fe-Co alloy using texture controlled technique,” Journal of Magnetism and Magnetic Materials, vol. 465, pp. 64-69, 2018. [4] F. Sanchez-De Jesus, A. Bolarin-Miro, C. Cortes Escobedo, G. Torres-Villasenor and P. Vera-Serna, “Structural Analysis and Magnetic Properties of FeCo Alloys Obtained by Mechanical Alloying,” Journal of Metallurgy, vol. 2016, p. 8347063, 2016. [5] R. Sundar and S. Deevi, “Soft magnetic FeCo alloys: alloy development, processing, and properties,” International Materials Reviews, vol. 50, no. 3, pp. 157-192, 2005. [6] Y. Zhang, R. Ma, S. Feng, L. Cheng, P. Davies and P. Yu, “Microstructures and magnetic properties of Fe-35%Co alloy fabricated bymetal injection molding,” Journal of Magnetism and Magnetic Materials, vol. 497, p. 165982, 2020.

**Images:**

![](https://assets.underline.io/uploads/markdown_image/1/image/b10699c413116d6f4d080b35248523dd.jpg)

![](https://assets.underline.io/uploads/markdown_image/1/image/a2da2cf697ccf1f003fbfd7cb478a821.jpg)

Magnetic Performance Improvement caused by Tensile Stress in Equivalent Iron Core fabricated by High-Strength Non-Oriented Electrical Steel

Next from INTERMAG 2021

Synthesis of α”-(Fe, M)16N2 nanoparticles obtained by hydrogen reduction and subsequent nitridation starting from α-(Fe, M)OOH (M= Co, Al)

Similar lecture

Study of Coherent Spin Waves in a Three-Dimensional Artificial Spin Ice Structure

Stay up to date with the latest Underline news!

PRESENTATIONS

CONFERENCES

COMPANY

RESOURCES