Metal Amorphous Nanocomposites (MANCs) are an evolving class of soft magnetic materials consisting of an Fe- or Co-based crystalline phase embedded in an amorphous matrix. In thin-film form, they possess highly tunable magnetic properties, low eddy current and hysteresis losses, and are capable of performing under high-frequency magnetic field reversal. Therefore they are good candidates for a range of applications including use in power electronics, transformers, and electric motors[1, 2]. We investigated the structural, static and dynamic properties of magnetron sputtered and vacuum annealed (5 minutes and 20 minutes at 520<sup>o</sup>C) films of CoFeMnNbSiB using Transmission Electron Microscopy (TEM), Atom Probe Tomography (APT), Vibrating Sample Magnetometry (VSM) and Ferro-Magnetic Resonance (FMR). The sputtered films did not show crystallinity, however, an Mn-rich columnar structure that spanned the thickness of the film parallel to the growth direction was observed. After annealing for 5 minutes and 20 minutes, the columnar structure transformed to a partially crystallized microstructure with Co and Fe enriched crystallized phases with ~7nm grain size enclosed by an amorphous intergranular region as shown in Fig. 1. The magnetization dynamics of the films were measured using a custom-built instrument with a frequency range of 1-65 GHz and fields up to 1.6 T. The FMR spectrum of annealed samples shows two overlapping resonances (Fig. 2) due to the two phases present in the samples whereas the as-sputtered sample shows only one resonance. The effective magnetization remained constant whereas the linewidth increased from 13 to 55 Oe after annealing. The magnetic coercivity was observed to be (~26 Oe) independent of annealing while the saturation magnetization increased from 828 to 953 emu/cm<sup>3</sup>. The observed changes in magnetic properties with annealing indicate that short-time annealing can be useful in optimizing the performance of these MANCs and tailoring properties for various applications.

![](https://assets.underline.io/uploads/markdown_image/1/image/8e0cc2fd197e33d1445aaa05db782123.jpg)

Fig. 1.a) TEM image of 20 minutes annealed sample b) Magnified section of a crystalline region

![](https://assets.underline.io/uploads/markdown_image/1/image/5a0af14f69f8ff951824fdad5f91dd49.jpg)

Fig. 2. FMR spectrum of 20 minutes annealed sample at 40 GHz reflecting two overlapping peaks due to dual-phase in the sample

Structural and magnetic characterization of Co-based soft magnetic amorphous nanocomposite films

**Session chair:** Ahmed Talaat, University of Pittsburgh



COA - Soft Magnetic Materials I: Amorphous and Nanocrystalline

technical paper

The 15th Joint MMM-INTERMAG Conference (2022 Joint) is sponsored jointly by AIP Publishing and the IEEE Magnetics Society. Members of the international scientific and engineering communities interested in recent developments in fundamental and applied magnetism are invited to attend and contribute to the technical sessions. The technical program will include invited and contributed papers in oral and poster sessions, invited symposia, a plenary session, and an evening session, with about 1500 presentations overall. This Conference provides an outstanding opportunity for worldwide participants to meet their colleagues and collaborators and discuss developments in all areas of magnetism research.

The 2022 Joint Conference will offer both in-person and prerecorded on-demand content.

For tickets to the event, please register at the following link: https://magnetism.org/register

Please register for the Joint MMM-Intermag conference to join the event.

2022 Joint MMM-INTERMAG

This Conference provides an outstanding opportunity for worldwide participants to meet their colleagues and collaborators and discuss developments in all areas of magnetism research.

Alicia Koenig

1

6

Presentations

Structural and magnetic characterization of Co-based soft magnetic amorphous nanocomposite films

Stay up to date with the latest Underline news!

PRESENTATIONS

CONFERENCES

COMPANY

RESOURCES