Advances in synthesis and characterization of magnetic nanoparticles (NPs) have yielded great gains in the understanding of their complex magnetic behaviour, with implications for numerous applications. Recent work using Ni NPs as a model soft ferromagnetic (FM) system achieved quantitative understanding of the superparamagnetic blocking temperature-particle diameter relationship1. This hinged, however, on the assumption of an FM NP volume lower than the chemical volume due to a non-FM surface dead shell, indirectly deduced from magnetometry. Here, we completely determine both the chemical and magnetic internal structure of such Ni NPs, via unpolarized, half-polarized, and fully-polarized small-angle neutron scattering (SANS) measurements and analyses, coupled with X-ray diffraction and magnetometry. The postulated magnetic dead shell is not only detected but conclusively identified as a Ni phosphide, derived from the trioctylphosphine commonly used in hot-injection syntheses. The shell thickness (t*) can be controlled by synthesis temperature (Ts), falling to as little as 0.5 nm at 170 °C (Fig. 1). Polarized SANS further reveals bulk-like ferromagnetism in the Ni core, the magnetic scattering length density (SLD) being in ideal agreement with magnetometry (Fig. 2), quantitatively supporting prior modeling of superparamagnetism. These findings advance the understanding of synthesis-structure-property relationships in metallic magnetic NPs, point to a route to ligand-free stabilization, and highlight the power of polarized SANS measurement and analysis capabilities for magnetic NP science and technology. Work supported by the UMN DOE Center for Quantum Materials.

![](https://assets.underline.io/uploads/markdown_image/1/image/d1fcb57216327d31778b53fae71eebc0.jpg)

Fig. 2. Ni core magnetic SLD vs. T (circles) from half-polarized SANS for the NPs at Ts = 170 °C, superimposed on magnetometry field-cooled (FC) (solid line) and zero field-cooled (ZFC) (dashed line) data measured at 50 Oe.


![](https://assets.underline.io/uploads/markdown_image/1/image/9a9b611d4e7684db8891288e9cd064ae.jpg)

Fig. 2. Ni core magnetic SLD vs. T (circles) from half-polarized SANS for the NPs at Ts = 170 °C, superimposed on magnetometry field-cooled (FC) (solid line) and zero field-cooled (ZFC) (dashed line) data measured at 50 Oe.

Chemically-induced Magnetic Dead Shells in Superparamagnetic Ni Nanoparticles from Polarized Small-Angle Neutron Scattering

**Session chair:** Victor Prida, University of Oviedo



EOC - Magnetic Nanostructures

technical paper

The 15th Joint MMM-INTERMAG Conference (2022 Joint) is sponsored jointly by AIP Publishing and the IEEE Magnetics Society. Members of the international scientific and engineering communities interested in recent developments in fundamental and applied magnetism are invited to attend and contribute to the technical sessions. The technical program will include invited and contributed papers in oral and poster sessions, invited symposia, a plenary session, and an evening session, with about 1500 presentations overall. This Conference provides an outstanding opportunity for worldwide participants to meet their colleagues and collaborators and discuss developments in all areas of magnetism research.

The 2022 Joint Conference will offer both in-person and prerecorded on-demand content.

For tickets to the event, please register at the following link: https://magnetism.org/register

Please register for the Joint MMM-Intermag conference to join the event.

2022 Joint MMM-INTERMAG

This Conference provides an outstanding opportunity for worldwide participants to meet their colleagues and collaborators and discuss developments in all areas of magnetism research.

Eray Aydil

1

1

Presentations

Chemically-induced Magnetic Dead Shells in Superparamagnetic Ni Nanoparticles from Polarized Small-Angle Neutron Scattering

Stay up to date with the latest Underline news!

PRESENTATIONS

CONFERENCES

COMPANY

RESOURCES